The catalyst was prepared under the following conditions: 5-25% solutions of zinc acetate and cadmium acetate and 1-3% solution of zirconyl nitrate were injected into the microspheric nanoparticle carrier (expanded clay) by circulating absorption at 60°C. The absorption time of the salts was varied between 60-90 minutes. Subsequent analysis of the IR spectrum showed that as the heating temperature of the sample increases, there will be changes in the IR spectra in the area of valence oscillations (2800-3900 cm-1) and in the area of deformation oscillations (4000-900 cm-1).